EPOXY based polymer of gloss and adhesion improver are suitable for wood and ceramic laminating and specially formulated for Jewellery , stone and wood coating and for colored MEENA application. And specially for stone / wood coating and filling crack and inlay applications. Ideally suitable for this application, provide clear, blush free, glossy, solvent free, high build coatings.

METHOD OF USE:- FOR SMALL ARTICALS (1) SURFACE PREPARATION:- Surface should be Dry, clean, even and free from dust, dirt, paint, rust, Algee, grease, soluble salt, or other contaminations and Damp free. (2) Heat the substrate / item that should be treated (3) Mix the polymer in proper ratio and remove bubbles by applying heat ( 40 oC) for some time and vacuum the bubbled Air. (4) Apply the mixed polymer clear / colored ( Add small drop quantity for light color and add more drop quantity for dark color in to the clear polymer. (5) Stoving should be done in closed oven for hard and glossy look. (6) Maintain temperature 40-60 oC for better results. Mix equal volumes of Part A and Part B. The two parts must be thoroughly mixed together to obtain a properly cured coating. The pot life of this system is about 20 -30 minutes. Coatings of this type should be applied to horizontal surfaces. The object to be coated should be elevated from the work surface by a pedestal smaller in diameter than the object so the coating can flow freely off the edges. As soon as the coating is mixed, it should be poured over the object and, if necessary, spread with a brush to ensure complete coverage. The bubbles created during mixing are typically broken by brushing the coating’s surface or by blowing on it using forced hot air. This high-gloss coating of 10 to 20 mils thickness will dry in about 7 hours at room temperature (~25oC) and will achieve its full hardness in 2 to 3 days. Color and gloss (i.e., lack of blush) are outstanding. Where a low HDT can be a problem (on tabletops, for example) a formulation containing less Note that clear coatings of this type should not be used on objects exposed to direct sunlight. General-purpose epoxy resins will yellow over time under such conditions.